Distortion Under Lamination & Dead Lock

Distortion Under Lamination & Dead Lock

  Title:Distortion Under Lamination & Dead Lock  Expression:
I am a technologist in making PVC cards, but now I met with such a problem that the PVC card would distort under lamination. Strangely, I seldom or even hardly plunged into this problem. The ineligible rate is about 2%. But this phenomenon happens not all the time but at times. Should the PVC be responsible for this problem? Moreover, this problem also arise when I use to same set of PVC to laminate. Will the laminator’s parameter cause the distortion? I usually set the high temperature at 160℃, the highest pressure at 14Mpa and a time of 40minutes or so. Is there anything with these parameters?
I think the dead lock problem has something to do with the sheet, but to what degree of pressure can the PVC sheet be laminated maxmumly.
I hope those who know the problem will tell me how to deal with it, and I will thank you sincerely to no end. Whoever is interested in this problem can join in its discussion.

Two points can account for this problem.
1,The temperature is set too high for the laminating sheet.
2,The materials including the basic printing sheet, PVCsheet and overlay film with glue, also differ in their melting point temperature.
The deadlock is always connected with the circuit breaker. 
First you should ascertian whether it is the control circuit system at the root of the problem or the break of electricity. The unstable of the system is responsible for the deadlock of the system, while the unstable supply of electricity should account for the break of electricity. If the supply of electricity is stable, you should consul with the manufacturer.
But this customer came up with the condition of using the same material and the problem arised as well. I think it is breakdown of the calefaction or heating up elements that affected the laminating effect. If one of the elements is not heated up, the laminated sheet will not bright in colour. But the rise of temperature will cause the sheet to distort. The temperature should not be set over 150℃, and the pressure not over 14-16mpa.